CTH:YAG
Chromium, Thulium, Holmium-Doped : Yttrium Aluminium Garnet Laser Crystals
CTH:YAG -yttrium aluminium garnet laser crystals doped with chromium, thulium and holmium ions to provide lasing at 2.13 microns are finding more and more applications, especially in the medical industry. The inherent advantage of the crystal is that it employs YAG as the host. YAG’s physical, thermal and optical properties are well known and understood by every laser designer.
Lasers operating at 2.13 microns couple well into water and body fluids, and can take advantage of using silica fibers for easy, accurate beam delivery. CTH:YAG can be readily Q-switched with either electro-optic material such as LiNbO3 or acousto-optics. Lasers using CTH:YAG are successfully used for medical procedures such as fragmentation of gallstones and for vascular welding.
Proprietary crystal preparation technology has been developed to overcome poor lasing efficiency, one of the major impediments to the use of laser materials in the 2 microns wavelength range. This technology allows production of CTH:YAG laser crystals with high optical quality, low scattering losses, and high efficiency. CTH:YAG laser crystals optimise the usefulness of the sensitiser ions for the holmium basing conditions at room temperature.
CTH:YAG laser crystals are offerred in sizes from 3 mm to 10 mm diameter, with lengths up to 150 mm long. Call upon our depth of experience in research, crystal growth and laser rod fabrication. Roditi will work with you to produce CTH:YAG laser crystals that meet the exact specifications for superior performance of your 2.13 microns laser system.
Applications
Designed for 2.13 µm output wavelength CTH:YAG is an excellent choice for Medical Laser Applications.
Optical and Laser Properties
| Laser
Action |
4
Level Laser |
Upper
Laser Level |
5I7 |
| Emission
Lifetime |
7.8
msec |
Lower
Level |
5I8 |
| Absorption
Bands |
Flashlamp
Pumped |
Refractive
Index |
1.8
at 632 nm |
| Output
Wavelength |
2.13 µm at 20°C flashlamp
pump |
Chemical
Formula |
Y3Al5O12:Cr,Tm,Ho |
| Emission
Cross-Section |
Σ = 0.98 x 10-20
cm2 |
CTH:YAG Laser Rod Standard Fabrication Specifications
| Feature | Standard | Special Order |
| Crystal
Orientation |
<111> within 5° | Available |
| Diameter | 3
mm to 10mm |
Available |
| Daimeter
Tolerance |
+0.0
mm/- 0.05 mm |
Available |
| Length
(plano/plano) |
30
mm to 150 mm |
Available |
| Length
Tolerance |
± 0.75 mm | ± 0.50 mm |
| Perpendiculairity
of End Faces (plano/plano) |
5
arc-minutes |
2
arc-minutes |
| Parallelism
of End Faces (plano/plano) |
10
arc-seconds |
|
| Flatness | 0.1
wave maximum |
0.10
wave maximum |
| (plano/plano) | over
90% of aperture |
over
full aperture |
| Surface
Finish at 5X |
20-10
(scratch & dig) |
10-5
(scratch & dig) |
| Barrel
Finish |
400
grit |
Polished
approx. 80-50 |
| End
Face Bevel |
0.075
mm to 0.12 mm at 45° angle |
|
| Chips | No
chips allowed on end face of rod; chip having maximum length of 0.3 mm permitted to lie in the area of bevel and barrel surfaces. |
|
| End
Configurations |
plano/plano,
plano/wedge, wedge/wedge or Brewster cut. Plano ends can be finished flat, concave or convex |
|
| Coatings | Standard
coating is AR at 2.13 µm with R<0.25% each face. Other coatings available. |
|